Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.90到2.10 g/cm³ |
| Apparent density | | ISO60 | 0.65到0.85 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.10到0.40 % |
| Water absorption rate | | ISO62 | <0.50 % |
| PostShrinkage | | ISO2577 | <0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 850 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >10.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 10到12 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 5.0到7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 8000到10000 MPa |
| Tensile stress | Injection | ISO527-2 | 50.0到70.0 MPa |
| Flexural modulus | Injection | ISO178 | 16000到19000 MPa |
| Bending stress | Injection | ISO178 | 140到160 MPa |
| compression stress | | ISO604 | 200到250 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25到35 kV/mm |
| | IEC60250 | 5.006.00 |
| | IEC60250 | 4.005.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | >200 °C |
| | ISO11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90到1.1 W/m/K |
| maximum service temperature | | IEC60216 | 210 °C |
| maximum service temperature | | IEC60216 | 170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.