Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Polyester SUPRAPLAST® UPA 63 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 注塑 | ISO 179/1eU | 10to12 kJ/m² |
| Charpy Notched Impact Strength | 注塑 | ISO 179/1eA | 5.0to7.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| Compression molding pressure | >10.0 MPa | ||
| Compression molding temperature | 165to180 °C |
| Electrical performance | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 25to35 kV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 5.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.030 |
| arc resistance | ASTM D495 | PLC 4 | |
| relative permittivity | 1MHz | IEC 60250 | 4.005.00 |
| Surface Resistivity | IEC 60093 | 1.0E+13到1.0E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010to0.030 |
| Mechanical properties | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| bending strength | 注塑 | ISO 178 | 140to160 MPa |
| Flexural modulus | 注塑 | ISO 178 | 16000to19000 MPa |
| compression stress | ISO 604 | 200to250 MPa | |
| tensile strength | 注塑 | ISO 527-2 | 50.0to70.0 MPa |
| Tensile modulus | 注塑 | ISO 527-2 | 8000to10000 MPa |
| flammability | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 850 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | <0.10 % | |
| Apparent density | ISO 60 | 0.65to0.85 g/cm³ | |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.50 % |
| Shrinkage rate | MD3 | ISO 2577 | 0.10to0.40 % |
| density | ISO 1183 | 1.90to2.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | RASCHIG GmbH/SUPRAPLAST® UPA 63 |
|---|---|---|---|
| maximum service temperature | 20,000h | IEC 60216 | 170 °C |
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | >200 °C |
| thermal conductivity | ASTME1461 | 0.90to1.1 W/m/K | |
| maximum service temperature | <50h | IEC 60216 | 210 °C |