PVDF SOLEF® 20810-32 SOLVAY USA
119
- Properties:high viscosity
- Usages:filmadhesive
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 比重 | ISO 1183 | 1.78 g/cm³ | |
| 收缩率 流动 | ASTM D995 | 2 % | |
| 收缩率 垂直 | ASTM D995 | 3 % | |
| 吸水率 23°C 24hr | ISO 62 | 0.04 % | |
| 熔体质量流动速率 | ASTM D1238 | 2 g/10min | |
| ASTM D1238 | 6 g/10min |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 退火 4.0mm | ASTM D648 | 62 °C | |
| ASTM D648 | 40 °C | ||
| 维卡软化温度 50°C/hr 10N | ISO 306 | 120 °C | |
| 熔融温度 | ASTM D3418 | 135 °C | |
| 玻璃转化温度 | -29 °C | ||
| 脆化温度 | ASTM D746 | -22 °C | |
| 导热系数 | JIS R2618 | 0.18 W/(m·K) | |
| 比热容 | 1200 J/(kg·°C) | ||
| 比热容 100°C | 1600 J/(kg·°C) | ||
| 结晶温度 | 92 | ||
| 平均熔解热 | 23 J/g | ||
| 24 J/g |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 23°C 1.0mm/min | ASTM D638 | 420 Mpa | |
| 拉伸强度 23°C 50mm/min | ASTM D638 | 40 Mpa | |
| 拉伸强度 屈服 23°C | ASTM D638 | 16.5 Mpa | |
| 伸长率 23°C | ASTM D638 | 675 % | |
| 伸长率 屈服 23°C 50mm/min | ASTM D638 | 13.5 % | |
| 弯曲强度 23°C | ASTM D790 | 40 Mpa | |
| 弯曲模量 23°C | ASTM D790 | 400 Mpa | |
| 悬臂梁缺口冲击 23°C | ASTM D256 | 180 J/m | |
| 摩擦系数 动态 | ASTM D3702 | 0.25 | |
| 摩擦系数 静态 | ASTM D3702 | 0.3 | |
| 泰伯尔磨损 | 10 mg/1000cy |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 表面电阻 | ASTM D257 | 100000000000000 Ω | |
| 氧指数 | ASTM D2863 | 54.5 % |
| 硬度 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 硬度 | 测试标准 | 数据 单位 | |
| 邵氏硬度D 2.0mm | ASTM D2240 | 60 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.