Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PVDF 20810-32 SOLVAY USA
SOLEF®
film、adhesive
high viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSOLVAY USA/20810-32
Peak Crystallization Temperature?92
Vicat Softening TemperatureISO 306120 °C
Glass Transition Temperature-29 °C
Peak Melting Temperature24 J/g
Specific Heat ( 100°C)1600 J/(kg·°C)
Deflection Temperature Under Load?(Annealed 4.0mm)ASTM D64840 °C
Specific Heat1200 J/(kg·°C)
Melting TemperatureASTM D3418135 °C
Thermal ConductivityJIS R26180.18 W/(m·K)
Brittleness TemperatureASTM D746-22 °C
HardnessTest ConditionTest MethodSOLVAY USA/20810-32
hardness测试标准数据 单位
Shore Hardness (Shore D)ASTM D224060
PhysicalTest ConditionTest MethodSOLVAY USA/20810-32
DensityISO 11831.78 g/cm³
Modeling Shrinkage (Flow)ASTM D9952 %
Melt Volume flow Rate (230°C 5kg)ASTM D12386 g/10min
Modeling Shrinkage (Across Flow)ASTM D9953 %
Moisture Absorption (23°C 24hr)ISO 620.04 %
Melt Mass-Flow Rate (230°C 2.16kg)ASTM D12382 g/10min
Mechanical PropertiesTest ConditionTest MethodSOLVAY USA/20810-32
Tensile Elongation (23°C)ASTM D638675 %
Notched Izod Impact Strength (23℃)ASTM D256180 J/m
Tensile Strength (23°C 50mm/min)ASTM D63840 Mpa
Tensile Elongation (Yield, 23°C, 50mm/min)ASTM D63813.5 %
Flexural Strength (23°C)ASTM D79040 Mpa
Flexural Modulus (23°C)ASTM D790400 Mpa
Coefficient of Friction (Dynamic)ASTM D37020.25
Taber Abrasion Resistance10 mg/1000cy
Tensile Modulus (23°C 1.0mm/min)ASTM D638420 Mpa
Tensile Strength (Yield 23°C)ASTM D63816.5 Mpa
Coefficient of Friction (Static)ASTM D37020.3
Electrical PropertiesTest ConditionTest MethodSOLVAY USA/20810-32
Surface ResistivityASTM D257100000000000000 Ω
Oxygen IndexASTM D286354.5 %