Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.14to1.15 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.40to0.50 % |
| Water absorption rate | Saturation | ASTM D570 | 4.0to5.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 115to125 |
| Shore hardness | | ASTM D2240 | 78to83 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2590to3960 MPa |
| tensile strength | | ASTM D638 | 72.4to79.3 MPa |
| elongation | Break | ASTM D638 | 35to55 % |
| Flexural modulus | | ASTM D790 | 2590to3280 MPa |
| bending strength | | ASTM D790 | 96.5to110 MPa |
| Compression Modulus | | ASTM D695 | 1900to2590 MPa |
| compressive strength | | ASTM D695 | 82.7to96.5 MPa |
| shear strength | | ASTM D732 | 55.2to62.1 MPa |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.12 |
| Heat distortion temperature | | ASTM D621 | 0.700to0.800 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 75to96 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.70 |
| dielectric strength | | ASTM D149 | 20to24 kV/mm |
| dielectric constant | | ASTM D150 | 3.70 |
| dielectric constant | | ASTM D150 | 3.70 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | | 227to238 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9E-05 cm/cm/°C |
| Usage temperature | | | 166 °C |
| Heat distortion temperature | | ASTM D648 | 210to216 °C |
| Heat distortion temperature | | ASTM D648 | 79.4to85.0 °C |
| Continuous use temperature | | ASTM D794 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.