Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.20to1.80 Pa·s |
| density | | | 1.70 g/cm³ |
| density | | | 1.78 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 92 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CriticalExposure | | | 6.90 mJ/cm² |
| Puncture Strength | | | 104.1 µm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 7600to11700 MPa |
| tensile strength | | ASTM D638 | 66.0to68.0 MPa |
| elongation | Break | ASTM D638 | 1.4to2.4 % |
| Flexural modulus | | ASTM D790 | 8300to9800 MPa |
| bending strength | | ASTM D790 | 124to154 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 13to17 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 65.0to66.0 °C |
| Heat distortion temperature | | ASTM D648 | 267to284 °C |
| Glass Transition Temperature | | DMA | 71.0to83.0 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 3.3E-5到4.4E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.1E-5到9.8E-5 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.