Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

Unspecified Bluestone 3D Systems
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256 | 13to17 J/m |
hardness | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
Shore hardness | 邵氏D | 92 |
Supplementary Information | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
Puncture Strength | 104.1 µm | ||
CriticalExposure | 6.90 mJ/cm² |
Mechanical properties | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 1.4to2.4 % |
tensile strength | ASTM D638 | 66.0to68.0 MPa | |
Tensile modulus | ASTM D638 | 7600to11700 MPa | |
Flexural modulus | ASTM D790 | 8300to9800 MPa | |
bending strength | ASTM D790 | 124to154 MPa |
physical property | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
density | --2 | 1.70 g/cm³ | |
--3 | 1.78 g/cm³ | ||
粘度(30°C) | 1.20to1.80 Pa·s |
Thermal performance | Test Condition | Test Method | 3D Systems/Bluestone |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火4,HDT | ASTM D648 | 65.0to66.0 °C |
0.45MPa,未退火5,HDT | ASTM D648 | 267to284 °C | |
Linear coefficient of thermal expansion | MD:0到200°C | ASTME831 | 3.3E-5到4.4E-5 cm/cm/°C |
Glass Transition Temperature | DMA | 71.0to83.0 °C | |
Linear coefficient of thermal expansion | MD:90到150°C | ASTME831 | 8.1E-5到9.8E-5 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火4,HDT | ASTM D648 | 65.0 °C |