PA66 TORZEN® G1300HS1L
72
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Fiber Content | ISO 3451/4 | 13 % | |
| Shrinkage rate | ISO 294-4 | 0.95 - 1.15 % | |
| ISO 294-4 | 0.45- 0.65 % | ||
| Water absorption rate | ISO 62 | 1.25 % | |
| ISO 62 | 1.9 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527 | 5600 Mpa | |
| tensile strength | ISO 527 | 117 Mpa | |
| elongation at break | ISO 527 | 2.6 % | |
| Flexural modulus | ISO 178 | 5200 Mpa | |
| bending strength | ISO 178 | 163 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 4 kJ/m² | |
| ISO 179 | 5 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180 | 5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75 | 256 °C | |
| ISO 75 | 240 °C | ||
| melting temperature | ISO 11357 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.