Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA66 G1300HS1L INVISTA USA
TORZEN®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | INVISTA USA/G1300HS1L |
---|---|---|---|
Charpy Notched Impact Strength | -40℃ | ISO 179 | 4 kJ/m² |
tensile strength | 断裂 | ISO 527 | 117 Mpa |
bending strength | ISO 178 | 163 Mpa | |
Flexural modulus | ISO 178 | 5200 Mpa | |
elongation at break | ISO 527 | 2.6 % | |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 5 kJ/m² |
Tensile modulus | ISO 527 | 5600 Mpa | |
Impact strength of cantilever beam gap | 23℃ | ISO 180 | 5 kJ/m² |
physical property | Test Condition | Test Method | INVISTA USA/G1300HS1L |
---|---|---|---|
Glass Fiber Content | ISO 3451/4 | 13 % | |
Shrinkage rate | 正常: 2.00 mm | ISO 294-4 | 0.95 - 1.15 % |
平行: 2.00 mm | ISO 294-4 | 0.45- 0.65 % | |
Water absorption rate | 23℃, 24 hr | ISO 62 | 1.25 % |
平衡, 23℃, 50% RH | ISO 62 | 1.9 % |
Thermal performance | Test Condition | Test Method | INVISTA USA/G1300HS1L |
---|---|---|---|
Heat distortion temperature | 0.45 MPa, 未退火,HDT | ISO 75 | 256 °C |
melting temperature | 10℃/min | ISO 11357 | 262 °C |
Heat distortion temperature | 1.82 MPa, 未退火,HDT | ISO 75 | 240 °C |