Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:70 |
| | | 2.0 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.13到1.17 g/cm³ |
| | | 0.40到0.60 Pa·s |
| Curing Time | | | 0.67到1.0 hr |
| STORAGE STABILITY | | | 5.0到7.0 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 77到83 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 1900到2300 MPa |
| Bending stress | | ISO178 | 90.0到110 MPa |
| compression stress | | ISO604 | 72.0到82.0 MPa |
| Tensile stress | | ISO527-2 | 67.0到77.0 MPa |
| Tensile strain | Break | ISO527-2 | 11到15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 63到87 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 127到133 °C |
| Glass Transition Temperature | | TMA | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.