Unspecified Ebalta MG 815 / Comp. A+B Ebalta Kunststoff GmbH
--
molding
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179 | 63to87 kJ/m² |
hardness | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Shore hardness | 邵氏D | ISO 7619 | 77to83 |
Mechanical properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
tensile strength | ISO 527-2 | 67.0to77.0 MPa | |
Tensile strain | 断裂 | ISO 527-2 | 11to15 % |
compression stress | ISO 604 | 72.0to82.0 MPa | |
Flexural modulus | ISO 178 | 1900to2300 MPa | |
bending strength | ISO 178 | 90.0to110 MPa |
thermosetting | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Thermosetting components | 按重量计算的混合比 | 100 | |
后固化时间(100°C) | 2.0 hr | ||
硬化法 | 按重量计算的混合比:70 |
Uncured Properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Viscosity | 25°C | 0.40to0.60 Pa·s | |
Curing Time | 70°C | 0.67to1.0 hr | |
STORAGE STABILITY | 20°C | 5.0to7.0 min | |
density | 20°C | 1.13to1.17 g/cm³ |
physical property | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Shrinkage rate | 内部方法 | 0.30 % |
Thermal performance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 815 / Comp. A+B |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 127to133 °C |
Glass Transition Temperature | TMA | 122 °C |