Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | | 1.00 cm³/g |
| density | | | 0.998 g/cm³ |
| Solid content by volume | | | 100 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 56000 cP |
| Thermosetting components | | | 15.0to20.0 min |
| Thermosetting components | | | 按容量计算的混合比:1.0按重量计算的混合比:1.0 |
| Thermosetting components | | | 按容量计算的混合比:1.0按重量计算的混合比:1.0 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 24 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 75 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Tensile shear adhesion | | ASTM D1002 | 8.96 MPa |
| Tensile shear adhesion | | ASTM D1002 | 20.7 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | | 5.0to15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact Strength | | | 35.7 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Usage temperature | | | -55-121 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.