LLDPE SABIC® 6821WE
58
- Properties:High hardness
- Usages:chipFood containers
CompareTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D-2457 | 45 ‰ | |
| Haze ratio | ASTM D-1003A | 20 % | |
| transparency | SABIC method | 20 mV |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 0.8 g/10min | |
| density | ISO 1183 | 921 kg/m3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Breaking stress | ISO 527-3 | 35 Mpa | |
| ISO 527-3 | 25 Mpa | ||
| elongation at break | ISO 527-3 | 520 % | |
| ISO 527-3 | 650 % | ||
| Elastic modulus | ISO 527-3 | 220 Mpa | |
| ISO 527-3 | 250 Mpa | ||
| ISO 8295 | 0.1 | ||
| Impact Strength | ASTM D-4272 | 30 KJ/m | |
| tear strength | ISO 6383-2 | 70 kN/m | |
| ISO 6383-2 | 350 kN/m | ||
| Anti puncture ability | SABIC method | 450 J/m | |
| yield stress | ISO 527-3 | 12.5 Mpa | |
| ISO 527-3 | 14 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| slip agent | SABIC method | 1500 mg/kg | |
| antiblocking agent | SABIC method | 3500 mg/kg | |
| antioxidant | SABIC method | + mg/kg | |
| Adhesive property | SABIC method | 10 g | |
| Posterior adhesion | SABIC method | ＜10 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B | 111 °C | |
| melting point | SABIC method | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.