Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 22 g/10 min |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 21.0 cm3/10min |
| Shrinkage rate - flow | | 内部方法 | 0.50 到 0.70 % |
| Shrinkage rate - flow | | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | | ISO 62 | 0.35 % |
| Water absorption rate | | ASTM D570 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 120 |
| Rockwell hardness | | ISO 2039-2 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 179/leA | 1.586 |
| transmissivity | | ASTM D1003 | 88.0 到 90.0 % |
| Haze ratio | | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2350 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2350 Mpa |
| tensile strength | | ASTM D638 | 63.0 Mpa |
| tensile strength | | ISO 527-2/50 | 63.0 Mpa |
| elongation | | ASTM D638 | 6.0 % |
| elongation | | ISO 527-2/50 | 6.0 % |
| elongation | | ASTM D638 | > 70 % |
| elongation | | ISO 527-2/50 | > 70 % |
| Flexural modulus | | ASTM D790 | 2300 Mpa |
| Flexural modulus | | ISO 178 | 2300 Mpa |
| Bending stress | | ISO 178 | 90.0 Mpa |
| Bending stress | | ASTM D790 | 90.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D4812, ISO 180/1U | 无断裂 |
| | ISO 180/1U | 无断裂 |
| Dart impact equipped with measuring instruments | | ASTM D3763 | 55.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257, IEC 60093 | > 1.0E+15 ohms·cm |
| dielectric strength | | ASTM D149, IEC 60243-1 | 27 KV/mm |
| dielectric constant | | ASTM D150, IEC 60250 | 3.00 |
| dielectric constant | | ASTM D150, IEC 60250 | 3.00 |
| Dissipation Factor | | ASTM D150, IEC 60250 | 1.0E-3 |
| Dissipation Factor | | ASTM D150, IEC 60250 | 0.010 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Hopper temperature | | | 60 到 80 °C |
| Temperature at the rear of the barrel | | | 260 到 280 °C |
| Temperature in the middle of the barrel | | | 270 到 290 °C |
| Temperature at the front of the material cylinder | | | 280 到 300 °C |
| Spray nozzle temperature | | | 270 到 290 °C |
| Processing (melt) temperature | | | 280 到 300 °C |
| Temperature | | | 80 到 100 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 133 °C |
| Thermal deformation temperature under load | | ISO 75-2/Bf | 133 °C |
| Thermal deformation temperature under load | | ASTM D648 | 122 °C |
| Thermal deformation temperature under load | | ISO 75-2/Af | 122 °C |
| vicat | | ISO 306/B50, ASTM D152510 | 140 °C |
| Ball Pressure Test | | IEC 60695-10-2 | 通过 |
| | ASTM E831 | 7.0E-5 cm/cm/°C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| thermal conductivity | | ASTM C177, ISO 8302 | 0.20 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.