Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2200RGC9AT SABIC INNOVATIVE SAUDI
SABIC®
--
High impact resistance、High temperature resistan、transparent、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 55.0 J |
| -30°C 8 | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 63.0 Mpa |
| Bending stress | -- 6, 7 | ISO 178 | 90.0 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| 断裂 | ISO 527-2/50 | > 70 % | |
| Flexural modulus | -- 6 | ISO 178 | 2300 Mpa |
| 50.0 mm 跨距 5 | ASTM D790 | 2300 Mpa | |
| elongation | 屈服 4 | ASTM D638 | 6.0 % |
| Bending stress | 屈服, 50.0 mm 跨距 5 | ASTM D790 | 90.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| -- 3 | ASTM D638 | 2350 Mpa | |
| tensile strength | 屈服 4 | ASTM D638 | 63.0 Mpa |
| elongation | 断裂 4 | ASTM D638 | > 70 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| dielectric strength | 1.60 mm | ASTM D149, IEC 60243-1 | 27 KV/mm |
| Volume resistivity | ASTM D257, IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric constant | 60 Hz | ASTM D150, IEC 60250 | 3.00 |
| Dissipation Factor | 1 MHz | ASTM D150, IEC 60250 | 0.010 |
| 60 Hz | ASTM D150, IEC 60250 | 1.0E-3 | |
| dielectric constant | 1 MHz | ASTM D150, IEC 60250 | 3.00 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| refractive index | ISO 179/leA | 1.586 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 到 90.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| Shrinkage rate - flow | -- 2 | 内部方法 | 0.50 到 0.70 % |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 21.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 22 g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| -40 到 95°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Bf | 133 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 122 °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 122 °C |
| 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 133 °C |
| thermal conductivity | ASTM C177, ISO 8302 | 0.20 W/m/K | |
| vicat | ISO 306/B50, ASTM D152510 | 140 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200RGC9AT |
|---|---|---|---|
| Temperature | 80 到 100 °C | ||
| Temperature at the rear of the barrel | 260 到 280 °C | ||
| Processing (melt) temperature | 280 到 300 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 280 到 300 °C | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Spray nozzle temperature | 270 到 290 °C | ||
| Hopper temperature | 60 到 80 °C | ||
| Temperature in the middle of the barrel | 270 到 290 °C |