Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.40-0.90 % |
| Water absorption rate | | ASTM D570 | 1.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 8340 Mpa |
| bending strength | | ASTM D790 | 255 Mpa |
| tensile strength | | ASTM D638 | 177 Mpa |
| elongation | | ASTM D638 | 3.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | 130 sec |
| Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 20 KV/mm |
| dielectric constant | | ASTM D150 | 3.80 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 210 °C |
| melting temperature | | ASTM D3418 | 220 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.