Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.5 % |
| Shrinkage rate | | ISO 294-4 | 1.2 % |
| Shrinkage rate | | ISO 294-4 | 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| Water absorption rate | | ISO 62 | 0.33 % |
| Water absorption rate | | ISO 62 | 0.14 % |
| MediumDensity | | | 1.37 g/cm³ |
| SpecificHeatCapacity of Melt | | | 1740 J/kg/°C |
| ThermalConductivityofMelt | | | 0.27 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | IEC 60695-11-10,-20 | V-0 |
| UL flame retardant rating | | IEC 60695-11-10,-20 | V-0 |
| Limiting Oxygen Index | | ISO 4589-2 | 31 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 44 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 53 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 32 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 33 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 7200 Mpa |
| tensile strength | | ISO 527-2 | 100 Mpa |
| Tensile strain | | ISO 527-2 | 3.4 % |
| Tensile creep modulus | | ISO 899-1 | 6000 Mpa |
| Tensile creep modulus | | ISO 899-1 | 4800 Mpa |
| bending strength | | ISO 178 | 155 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 28 KV/mm |
| relative permittivity | | IEC 60250 | 3.70 |
| relative permittivity | | IEC 60250 | 3.50 |
| Dissipation Factor | | IEC 60250 | 3E-03 |
| Dissipation Factor | | IEC 60250 | 0.017 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 218 °C |
| Heat distortion temperature | | ISO 75-2/A | 203 °C |
| vicat | | ISO 306/B50 | 207 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.