PBT SK643FR-NC010 DUPONT BELGIUM
Crastin®
Electronic and electrical、Automotive Applications
Flame retardant、Glass fiber reinforced、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 32 kJ/m² |
| 23°C | ISO 180/1U | 33 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 53 kJ/m² |
| -30°C | ISO 179/1eU | 44 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.70 |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.017 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 7200 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 6000 Mpa |
| bending strength | ISO 178 | 155 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.4 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 4800 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 100 Mpa |
| flammability | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | V-0 |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 31 % |
| physical property | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr,2.00mm | ISO 62 | 0.33 % |
| Shrinkage rate | TD | ISO 294-4 | 1.2 % |
| MD | ISO 294-4 | 0.70 % | |
| MediumDensity | 1.37 g/cm³ | ||
| Shrinkage rate | MD2 | ISO 294-4 | 0.80 % |
| SpecificHeatCapacity of Melt | 1740 J/kg/°C | ||
| ThermalConductivityofMelt | 0.27 W/m/K | ||
| Shrinkage rate | TD2 | ISO 294-4 | 1.5 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.14 % |
| Thermal performance | Test Condition | Test Method | DUPONT BELGIUM/SK643FR-NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 218 °C |
| vicat | ISO 306/B50 | 207 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 203 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |