Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| viscosity number | | ISO 307 | 196 cm³/g |
| density | | ISO 1183 | 1.13 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | 内部方法 | 83.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Puncture Resistance | | 内部方法 | 13.0 J/cm |
| Relative solution viscosity (RSV) | | 内部方法 | 3.03 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ISO 8295 | 1.0 |
| coefficient of friction | | ISO 8295 | 1.2 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | 内部方法 | 810 Pa·s |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ISO 527-3 | 350 % |
| Tear strength of pants shape | | ISO 6383-1 | 32.0 N/mm |
| film thickness | | | 50 µm |
| Tensile modulus | | 内部方法 | 455 MPa |
| Tensile stress | | ISO 527-3 | 31.0 MPa |
| Tensile stress | | ISO 527-3 | 82.0 MPa |
| OTr | | DIS15105-1/-2 | 38 cm³/m²/bar/24hr |
| Water Vapor Transmission Rate | | DIS15106-1/-3 | 35 g/m²/24hr |
| OTr | | DIS15105-1/-2 | 26 cm³/m²/bar/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
| Specific heat capacity | | | 1550 J/kg/°C |
| Specific heat capacity | | | 2250 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.