PA6 F130-C3 DSM Additive Manufacturing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Supplementary InformationTest ConditionTest MethodDSM Additive Manufacturing/ F130-C3
Puncture Resistance50.0µm内部方法13.0 J/cm
Relative solution viscosity (RSV)内部方法3.03
filmTest ConditionTest MethodDSM Additive Manufacturing/ F130-C3
Tensile stress屈服,50µm,铸造薄膜，MDISO 527-331.0 MPa
OTr85%RH:23°C,50.0µmDIS15105-1/-238 cm³/m²/bar/24hr
elongation断裂,50µm,铸造薄膜ISO 527-3350 %
Tear strength of pants shape50µm,CastFilm，MDISO 6383-132.0 N/mm
film thickness50 µm
Water Vapor Transmission Rate23°C,85%RH,50µm,铸造薄膜DIS15106-1/-335 g/m²/24hr
OTr0%RH:23°C,50.0µmDIS15105-1/-226 cm³/m²/bar/24hr
Tensile modulus50µm,铸造薄膜内部方法455 MPa
Tensile stress50µm,铸造薄膜，MDISO 527-382.0 MPa
Mechanical propertiesTest ConditionTest MethodDSM Additive Manufacturing/ F130-C3
coefficient of friction与自身-静态,铸造薄膜ISO 82951.2
与自身-动态,铸造薄膜ISO 82951.0
optical performance Test ConditionTest MethodDSM Additive Manufacturing/ F130-C3
transmissivity50.0µm,铸造薄膜内部方法83.0 %
Filling analysisTest ConditionTest MethodDSM Additive Manufacturing/ F130-C3
melt viscosity260°C内部方法810 Pa·s
physical property Test ConditionTest MethodDSM Additive Manufacturing/ F130-C3
viscosity numberISO 307196 cm³/g
densityISO 11831.13 g/cm³
Thermal performanceTest ConditionTest MethodDSM Additive Manufacturing/ F130-C3
Specific heat capacityAverage:20到150°C2250 J/kg/°C
--1550 J/kg/°C
Linear coefficient of thermal expansionMDISO 11359-29E-05 cm/cm/°C