Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.15 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 17.0 cm³/10min |
| Shrinkage rate | | 内部方法 | 0.40to0.60 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 120 |
| ball-indentation hardness | | ISO 2039-1 | 106 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 2400 MPa |
| fracture | | ISO 527-2/50 | >50 % |
| bending strength | | ISO 178 | 85.0 MPa |
| Taber abraser | | 内部方法 | 95.0 mg |
| Tensile modulus | | ISO 527-2/1 | 2500 MPa |
| yield | | ISO 527-2/5 | 55.0 MPa |
| yield | | ISO 527-2/50 | 62.0 MPa |
| fracture | | ISO 527-2/5 | 60.0 MPa |
| fracture | | ISO 527-2/50 | 62.0 MPa |
| yield | | ISO 527-2/5 | 5.0 % |
| yield | | ISO 527-2/50 | 4.0 % |
| fracture | | ISO 527-2/5 | 130 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 kV/mm |
| relative permittivity | | IEC 60250 | 2.80 |
| Dissipation Factor | | IEC 60250 | 0.013 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare