Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA+PC GELOY™ HRA170 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| -30°C | ISO 179/1eA | 12 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| 23°C | ISO 180/1A | 45 kJ/m² |
| hardness | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 106 MPa |
| Mechanical properties | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| fracture | ISO 527-2/50 | 62.0 MPa | |
| ISO 527-2/50 | >50 % | ||
| yield | ISO 527-2/50 | 4.0 % | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 95.0 mg |
| fracture | ISO 527-2/5 | 60.0 MPa | |
| yield | ISO 527-2/5 | 5.0 % | |
| Flexural modulus | ISO 178 | 2400 MPa | |
| yield | ISO 527-2/5 | 55.0 MPa | |
| Tensile modulus | ISO 527-2/1 | 2500 MPa | |
| fracture | ISO 527-2/5 | 130 % | |
| bending strength | ISO 178 | 85.0 MPa | |
| yield | ISO 527-2/50 | 62.0 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 kV/mm |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.013 |
| flammability | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| Burning wire flammability index | 3.20mm | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 22 % |
| physical property | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.60 % | |
| density | ISO 1183 | 1.15 g/cm³ | |
| Shrinkage rate | MD1 | 内部方法 | 0.40to0.60 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 17.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | SABIC/GELOY™ HRA170 resin |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |