PEI ULTEM™ AUT200 BK
100
- Properties:High mobilityHigh transparencyhigh definition
- Usages:Electrical appliancesAutomotive Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 18 g/10min | |
| Melt volume flow rate | ISO 1133 | 25.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | ISO 62 | 1.3 % | |
| ISO 62 | 0.70 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Metallic haze | 内部方法 | 204 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 3520 Mpa | |
| Tensile modulus | ASTM D638 | 3590 Mpa | |
| ISO 527-2/1 | 3200 Mpa | ||
| tensile strength | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 105 Mpa | ||
| ASTM D638 | 105 Mpa | ||
| ISO 527-2/5 | 85.0 Mpa | ||
| elongation | ASTM D638 | 7.0 % | |
| Tensile strain | ISO 527-2/5 | 6.0 % | |
| elongation | ASTM D638 | 60 % | |
| Tensile strain | ISO 527-2/5 | 60 % | |
| Flexural modulus | ISO 178 | 3300 Mpa | |
| bending strength | ISO 178 | 160 Mpa | |
| ASTM D790 | 165 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.0 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 5.0 kJ/m² | |
| ISO 180/1A | 5.0 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 33.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 5.5E-05 cm/cm/°C | |
| ISO 11359-2 | 5E-05 cm/cm/°C | ||
| ASTME831 | 5.5E-05 cm/cm/°C | ||
| ISO 11359-2 | 5E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 205 °C | |
| ASTM D648 | 197 °C | ||
| ASTM D648 | 199 °C | ||
| ISO 75-2/Ae | 190 °C | ||
| ISO 75-2/Af | 193 °C | ||
| vicat | ASTM D152511 | 219 °C | |
| ISO 306/B50 | 211 °C | ||
| ISO 306/B120 | 212 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.