PEI AUT200 BK SABIC INNOVATIVE US
ULTEM™
Electrical appliances、Automotive Applications
High mobility、High transparency、high definition
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/AUT200 BK |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 199 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 211 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 205 °C |
| Linear thermal expansion coefficient | TD：23to150°C | ISO11359-2 | 5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,100mm跨距9 | ISO75-2/Ae | 190 °C |
| Linear thermal expansion coefficient | TD：-40to150°C | ASTME831 | 5.5E-05 cm/cm/°C |
| Vicat Softening Temperature | ASTMD152511 | 219 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 197 °C |
| Linear thermal expansion coefficient | MD：-40to150°C | ASTME831 | 5.5E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B120 | 212 °C |
| Linear thermal expansion coefficient | MD：23到150°C | ISO11359-2 | 5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 193 °C |
| Additional | Test Condition | Test Method | SABIC INNOVATIVE US/AUT200 BK |
|---|---|---|---|
| MetallizedHazeOnset | 内部方法 | 204 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/AUT200 BK |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.70 % |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 25.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 18 g/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 1.3 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/AUT200 BK |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3520 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 60 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 60 % |
| Tensile Modulus | ISO527-2/1 | 3200 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 110 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 85.0 Mpa |
| Flexural Modulus | ISO178 | 3300 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 165 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 7.0 % |
| Flexural Strength | ISO178 | 160 Mpa | |
| Tensile Modulus | ASTMD638 | 3590 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 105 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 6.0 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 105 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/AUT200 BK |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 5.0 kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 33.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.0 kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 5.0 kJ/m² |