Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.07 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 14.0 cm³/10min |
| Shrinkage rate | | ISO 2577 | 0.65to0.75 % |
| Shrinkage rate | | ISO 2577 | 0.65to0.75 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 90.0 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | <40 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Total Carbon Emissions | | VDA277 | <25.0 µgC/g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA278 | <5.00 µg/g |
| Emission | | VDA278 | <10.0 µg/g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 2000 MPa |
| bending strength | | ISO 178 | 68.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 2000 MPa |
| tensile strength | | ISO 527-2/50 | 42.0 MPa |
| Tensile strain | | ISO 527-2/50 | 7.0 % |
| Tensile strain | | ISO 527-2/50 | 53 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | 20 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 40 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 53 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 41 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 58 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B120 | 115 °C |
| Heat distortion temperature | | ISO 75-2/B | 113 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.9E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 101 °C |
| vicat | | ISO 306/B50 | 113 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.