ABS Ultra HH 4115 HI ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 53 kJ/m² |
-30°C | ISO 179/1eA | 40 kJ/m² | |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 41 kJ/m² |
23°C | ISO 180/1A | 58 kJ/m² |
hardness | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 90.0 MPa |
Supplementary Information | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
Emission | FOGtotal:23°C | VDA278 | <5.00 µg/g |
VOCtotal:23°C | VDA278 | <10.0 µg/g |
Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
tensile strength | 屈服,23°C | ISO 527-2/50 | 42.0 MPa |
Flexural modulus | 23°C | ISO 178 | 2000 MPa |
Tensile strain | 屈服,23°C | ISO 527-2/50 | 7.0 % |
断裂,23°C | ISO 527-2/50 | 53 % | |
Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 20 % |
Tensile modulus | 23°C | ISO 527-2/1 | 2000 MPa |
bending strength | 23°C | ISO 178 | 68.0 MPa |
flammability | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
Total Carbon Emissions | 23°C | VDA277 | <25.0 µgC/g |
burning rate | 2.00mm | ISO 3795 | <40 mm/min |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
density | 25°C | ISO 1183 | 1.07 g/cm³ |
Shrinkage rate | TD | ISO 2577 | 0.65to0.75 % |
MD | ISO 2577 | 0.65to0.75 % | |
Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 14.0 cm³/10min |
Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./Ultra HH 4115 HI |
---|---|---|---|
vicat | -- | ISO 306/B120 | 115 °C |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 8.9E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 101 °C |
vicat | -- | ISO 306/B50 | 113 °C |
Heat distortion temperature | 0.45MPa,退火,HDT | ISO 75-2/B | 113 °C |