POM/PTFE LNP™ LUBRICOMP™ KAL-4022 BK
33
- Properties:heat-resistinghigh strengthGlass fiber reinforced
- Usages:Automotive Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 1.8to2.2 % | |
| ASTMD955 | 2.0to4.0 % | ||
| ASTMD955 | 2.0to4.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus 6 | ISO178 | 3080 Mpa | |
| Bending stress | ISO178 | 77.0 Mpa | |
| ASTMD3702Modified | 0.23 | ||
| ASTMD3702Modified | 0.16 | ||
| Wear factor | ASTMD3702Modified | 0.00 10^-10in^5-min/ft-lb-hr | |
| ASTMD3702Modified | 8.00 10^-10in^5-min/ft-lb-hr | ||
| Tensile modulus 3 | ASTMD638 | 3640 Mpa | |
| Tensile modulus | ISO527-2/1 | 3460 Mpa | |
| Tensile stress | ISO527-2/5 | 57.0 Mpa | |
| Tensile strength 4 | ASTMD638 | 58.0 Mpa | |
| Tensile stress | ISO527-2/5 | 56.0 Mpa | |
| elongation | ASTMD638 | 6.5 % | |
| Tensile strain | ISO527-2/5 | 6.3 % | |
| elongation | ASTMD638 | 7.4 % | |
| Tensile strain | ISO527-2/5 | 7.4 % | |
| Flexural modulus | ASTMD790 | 3090 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| NotchedIzodImpactStrength7 | ISO180/1A | 5.5 kJ/m² | |
| UnnotchedIzodImpactStrength7 | ISO180/1U | 32 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 162 °C | ||
| ASTMD648 | 132 °C | ||
| ISO75-2/Af | 87.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.