Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM/PTFE KAL-4022 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting、high strength、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 32 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3460 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 56.0 Mpa |
| elongation | 屈服 | ASTM D638 | 6.5 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 6.3 % |
| Wear factor | Washer | ASTM D3702Modified | 8.00 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 3090 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 57.0 Mpa |
| Tensile modulus | ASTM D638 | 3640 Mpa | |
| elongation | 断裂 | ASTM D638 | 7.4 % |
| tensile strength | Break | ASTM D638 | 58.0 Mpa |
| bending strength | ISO 178 | 77.0 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.16 |
| Flexural modulus | ISO 178 | 3080 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 7.4 % |
| Wear factor | Ring | ASTM D3702Modified | 0.00 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.23 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 BK |
|---|---|---|---|
| Shrinkage rate | MD：24hr | ASTM D955 | 2.0-4.0 % |
| MD：--2 | 内部方法 | 1.8-2.2 % | |
| TD：24hr | ASTM D955 | 2.0-4.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 162 °C |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 87.0 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 132 °C |