PA610 LNP™ THERMOCOMP™ QF-100-10 SABIC INNOVATIVE US
137
- Properties:Glass fiber reinforcedThermal stability
- Usages:Electronic and ElectricalPlastic bag
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 收缩率 | MD：24小时 | ASTMD955 | 0.18to0.20 % |
| TD：24hr | ASTMD955 | 0.50to1.5 % | |
| 吸水率 | 24hr,50%RH | ASTMD570 | 0.21 % |
| 平衡,23°C,50%RH | ISO62 | 0.28 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 221 °C |
| 热变形温度7 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 220 °C |
| 热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 213 °C |
| 热变形温度7 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 206 °C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 18700 Mpa | |
| 弯曲模量 | ISO178 | 12900 Mpa | |
| 弯曲强度 | 屈服,50.0mm跨距 | ASTMD790 | 280 Mpa |
| 弯曲强度5 | 断裂,50.0mm跨距 | ASTMD790 | 285 Mpa |
| 拉伸模量 | ISO527-2/1 | 15500 Mpa | |
| 抗张强度 | 屈服 | ASTMD638 | 181 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/5 | 182 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 181 Mpa |
| 拉伸应力 | 断裂 | ISO527-2/5 | 182 Mpa |
| 伸长率 | 屈服 | ASTMD638 | 2.6 % |
| 拉伸应变 | 屈服 | ISO527-2/5 | 2.3 % |
| 伸长率 | 断裂 | ASTMD638 | 2.6 % |
| 拉伸应变 | 断裂 | ISO527-2/5 | 2.3 % |
| 弯曲模量 | 50.0mm跨距 | ASTMD790 | 11400 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 悬壁梁缺口冲击强度6 | 23°C | ISO180/1A | 14 kJ/m² |
| 无缺口伊佐德冲击强度5 | 23°C | ISO180/1U | 75 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.