PA610 QF-100-10 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical、Plastic bag
Glass fiber reinforced、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/QF-100-10 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 75 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/QF-100-10 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 15500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 182 Mpa |
| elongation | 屈服 | ASTM D638 | 2.6 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.3 % |
| tensile strength | 断裂 | ASTM D638 | 181 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 11400 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 182 Mpa |
| Tensile modulus | ASTM D638 | 18700 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 280 Mpa |
| elongation | 断裂 | ASTM D638 | 2.6 % |
| Flexural modulus | ISO 178 | 12900 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.3 % |
| tensile strength | 屈服 | ASTM D638 | 181 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 285 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/QF-100-10 |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.18-0.20 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.21 % |
| 平衡,23°C,50%RH | ISO 62 | 0.28 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.50-1.5 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/QF-100-10 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 220 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 221 °C | |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 206 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 213 °C |