Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.31 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Shrinkage rate | | 内部方法 | 1.7 % |
| Water absorption rate | | ASTM D570 | 0.050 % |
| Water absorption rate | | ISO 62 | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 100 % |
| Flexural modulus | | ASTM D790 | 2500 MPa |
| bending strength | | ASTM D790 | 87.0 MPa |
| Tensile modulus | | ASTM D638 | 2550 MPa |
| tensile strength | Yield | ASTM D638 | 52.0 MPa |
| tensile strength | Break | ASTM D638 | 34.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 45 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+14 ohms |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 3.20 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 55.0 °C |
| vicat | | ASTM D15253 | 175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare