PBT Pibiter® N200 NAT001 SO.F.TER ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 45 J/m |
| Electrical performance | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| dielectric constant | 1kHz | ASTM D150 | 3.20 |
| Volume resistivity | 23°C | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | 1.60mm | ASTM D149 | 17 kV/mm |
| Mechanical properties | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 100 % |
| Flexural modulus | ASTM D790 | 2500 MPa | |
| Tensile modulus | ASTM D638 | 2550 MPa | |
| tensile strength | 断裂 | ASTM D638 | 34.0 MPa |
| 屈服 | ASTM D638 | 52.0 MPa | |
| bending strength | ASTM D790 | 87.0 MPa |
| flammability | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 20 g/10min |
| Shrinkage rate | 内部方法 | 1.7 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.35 % |
| 23°C,24hr | ASTM D570 | 0.050 % | |
| density | ASTM D792 | 1.31 g/cm³ |
| Thermal performance | Test Condition | Test Method | SO.F.TER ITALY/Pibiter® N200 NAT001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 55.0 °C |
| vicat | ASTM D15253 | 175 °C |