Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.900 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| melt mass-flow rate | | ISO 1133 | 8.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 80 |
| Rockwell hardness | R-Scale | ISO 2039-2 | 82 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | <2.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HeatSealTemperature | | 内部方法 | 120 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 21.6 MPa |
| tensile strength | Yield | ISO 527-2 | 22.6 MPa |
| elongation | Break | ASTMD638 | >500 % |
| Flexural modulus | | ASTM D790 | 735 MPa |
| Flexural modulus | | ISO 178 | 785 MPa |
| coefficient of friction | | 内部方法 | <1.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 98 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 70.0 °C |
| melting temperature | | 内部方法 | 132 °C |
| melting temperature | | ASTM D3418 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.