Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Terpolymer RANPELEN SFC-750D LOTTE KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 98 J/m |
| Supplementary Information | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| HeatSealTemperature | 30.0µm | 内部方法 | 120 °C |
| hardness | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 82 |
| R级 | ASTM D785 | 80 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | >500 % |
| Flexural modulus | -- | ISO 178 | 785 MPa |
| tensile strength | 屈服 | ASTM D638 | 21.6 MPa |
| 屈服 | ISO 527-2 | 22.6 MPa | |
| coefficient of friction | 铸造薄膜 | 内部方法 | <1.0 |
| Flexural modulus | -- | ASTM D790 | 735 MPa |
| optical performance | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| Haze ratio | 30.0µm,铸造薄膜 | ASTM D1003 | <2.0 % |
| physical property | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| density | ASTMD792 | 0.900 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 7.0 g/10min |
| 230°C/2.16kg | ISO 1133 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/RANPELEN SFC-750D |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTMD648 | 70.0 °C |
| melting temperature | -- | 内部方法 | 132 °C |
| -- | ASTM D3418 | 130 °C |