ABS

ABS MAGNUM™ 375 HP Trinseo

Usages:
Applications in the automotive field automotive internal components
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,PeakEnergy	ASTM D3763	30.0 J
Dart impact	Dart impact	-30°C,PeakEnergy	ASTM D3763	23.0 J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	22 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	130 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	220 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/A	10 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	25 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	47.0 MPa
tensile strength	tensile strength	Yield	ASTM D638	49.0 MPa
Tensile modulus		ISO 527-2	2330 MPa
Tensile modulus	Tensile modulus		ASTM D638	2300 MPa
Bending modulus		ISO 178	2390 MPa
Bending modulus	Bending modulus		ASTM D790	2410 MPa
Tensile strain	Break	ISO 527-2/50	3.5 %
elongation	Break	ASTM D638	8.8 %
Tensile strain	Yield	ISO 527-2/50	2.9 %
elongation	Yield	ASTM D638	3.1 %
bending strength		ASTM D790	76.5 MPa
bending strength	bending strength		ISO 178	72.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	81.7 °C
Linear coefficient of thermal expansion	TD：-40to100°C	ASTME831	9.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to100°C	ASTME831	7.7E-05 cm/cm/°C
Vicat softening temperature		ISO 306/B50	103 °C
Vicat softening temperature	Vicat softening temperature		ASTM D15257	103 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	83.9 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	98.0 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	99.4 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	0.56 %
melt mass-flow rate	230°C/3.8kg	ISO 1133	2.1 g/10min
melt mass-flow rate	melt mass-flow rate	230°C/3.8kg	ASTM D1238	2.1 g/10min
Apparent density		ASTM D1895	0.68 g/cm³
density		ISO 1183/B	1.06 g/cm³
density	density		ASTM D792	1.06 g/cm³
Shrinkage rate	MD	ISO 294-4	0.57 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.