Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MAGNUM™ 375 HP Trinseo
--
Applications in the automotive field, automotive internal components
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/MAGNUM™ 375 HP |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 22 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 130 J/m |
| 23°C | ASTM D256 | 220 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Dart impact | -30°C,PeakEnergy | ASTM D3763 | 23.0 J |
| 23°C,PeakEnergy | ASTM D3763 | 30.0 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 25 kJ/m² |
| -30°C | ISO 180/A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Trinseo/MAGNUM™ 375 HP |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 8.8 % |
| 屈服 | ASTM D638 | 3.1 % | |
| Flexural modulus | ASTM D790 | 2410 MPa | |
| Tensile modulus | ASTM D638 | 2300 MPa | |
| ISO 527-2 | 2330 MPa | ||
| tensile strength | 屈服 | ASTM D638 | 49.0 MPa |
| Flexural modulus | ISO 178 | 2390 MPa | |
| bending strength | ASTM D790 | 76.5 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.5 % |
| 屈服 | ISO 527-2/50 | 2.9 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 47.0 MPa |
| bending strength | ISO 178 | 72.0 MPa |
| physical property | Test Condition | Test Method | Trinseo/MAGNUM™ 375 HP |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.56 % |
| MD | ISO 294-4 | 0.57 % | |
| density | ISO 1183/B | 1.06 g/cm³ | |
| Apparent density | ASTM D1895 | 0.68 g/cm³ | |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 2.1 g/10min |
| 230°C/3.8kg | ISO 1133 | 2.1 g/10min | |
| density | ASTM D792 | 1.06 g/cm³ |
| Thermal performance | Test Condition | Test Method | Trinseo/MAGNUM™ 375 HP |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 81.7 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 99.4 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 98.0 °C | |
| Linear coefficient of thermal expansion | MD：-40to100°C | ASTME831 | 7.7E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 103 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 83.9 °C |
| Linear coefficient of thermal expansion | TD：-40to100°C | ASTME831 | 9.5E-05 cm/cm/°C |
| vicat | ASTM D15257 | 103 °C |