Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.41 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 2.5 g/10min |
| Melt volume flow rate | | ISO 1133 | 2.20 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 2.0 % |
| Water absorption rate | | ISO 62 | 0.80 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 140 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| burning rate | | FMVSS302 | <100 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO 1874 | POM-K.M-GNR.01-02 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2600 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 14 % |
| Tensile strain | Break | ISO 527-2/50 | 50 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 60.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 200 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 8.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 8.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 25 kV/mm |
| dielectric constant | | IEC 60250 | 3.80 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B | 150 °C |
| melting temperature | | ISO 11357-3 | 167 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Short term use temperature | | | 100 °C |
| Heat distortion temperature | | ISO 75-2/A | 105 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare