POM Copolymer Tarnoform® 200 Grupa Azoty ATT Polymers GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | ISO 180 | 8.0 kJ/m² | |
| Charpy Notched Impact Strength | -- | ISO 179/1eA | 8.5 kJ/m² |
| Impact strength of simply supported beam without notch | -- | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 200 kJ/m² |
| hardness | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 140 MPa |
| Supplementary Information | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| ISOType | ISO 1874 | POM-K.M-GNR.01-02 |
| Electrical performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 25 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| dielectric constant | 1Hz | IEC 60250 | 3.80 |
| Mechanical properties | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2400 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 50 % |
| Tensile modulus | ISO 527-2/1 | 2600 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 14 % |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| bending strength | ISO 178 | 60.0 MPa |
| flammability | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.20 cm³/10min |
| Shrinkage rate | MD：2.00mm | ISO 294-4 | 2.0 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.5 g/10min |
| Thermal performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnoform® 200 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 167 °C | |
| vicat | ISO 306/B | 150 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Short term use temperature | 100 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C |