Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD4669 | 1.10 g/cm³ |
| Shrinkage rate | | ASTMD2566 | 0.10到0.30 % |
| Weight Percubicinch | | | 18 g |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 按重量计算的混合比:100,按容量计算的混合比:120 |
| Thermosetting mixed viscosity | | ASTMD4878 | 250到350 cP |
| stripping time | | 内部方法 | 240到360 min |
| GelTime | | ASTMD2971 | 25.0 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 1000 MPa |
| tensile strength | | ASTMD638 | 53.1 MPa |
| elongation | Break | ASTMD638 | 8.6 % |
| Flexural modulus | | ASTMD790 | 2160 MPa |
| bending strength | | ASTMD790 | 82.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 43 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 480 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 70.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.