TP, Unspecified Ultralloy™ 108 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 480 J/m | |
| Impact strength of cantilever beam gap | ASTM D256 | 43 J/m |
| hardness | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 80 |
| Mechanical properties | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 8.6 % |
| tensile strength | ASTM D638 | 53.1 MPa | |
| Tensile modulus | ASTM D638 | 1000 MPa | |
| Flexural modulus | ASTM D790 | 2160 MPa | |
| bending strength | ASTM D790 | 82.0 MPa |
| thermosetting | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| Thermosetting mixed viscosity | 25°C | ASTM D4878 | 250to350 cP |
| GelTime | 25°C | ASTM D2971 | 25.0 min |
| stripping time | 21°C | 内部方法 | 240to360 min |
| Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
| 部件B | 按重量计算的混合比:100.按容量计算的混合比:120 |
| physical property | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D2566 | 0.10to0.30 % |
| density | ASTM D4669 | 1.10 g/cm³ | |
| Weight Percubicinch | 18 g |
| Thermal performance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 108 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 70.0 °C |