Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.40to0.60 % |
| Shrinkage rate | | 内部方法 | 0.20to0.40 % |
| Water absorption rate | | ISO62 | 0.14 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 4000 Mpa |
| Tensile stress | | ISO527-2/5 | 65.0 Mpa |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Bending modulus 2 | | ISO178 | 4400 Mpa |
| Bending stress 2 | | ISO178 | 110 Mpa |
| elongation at break | | ASTM D638/ISO 527 | 3.0 % |
| Tensile modulus | | ASTM D638/ISO 527 | 4000 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 4400 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 3.40 |
| Dissipation Factor | | IEC60250 | 1E-03 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| CTI | | IEC60112 | 175 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Dielectric strength 3 | | IEC60243-1 | 35 KV/mm |
| | IEC60250 | 3.40 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.14 |
| Mold Shrinkage | | ASTM D955 | 0.2-0.4 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 131 °C |
| | ISO75-2/A | 123 °C |
| vicat | | ISO306/B50 | 135 °C |
| | ISO11359-2 | 4E-05 cm/cm/°C |
| | ISO11359-2 | 6E-05 cm/cm/°C |
| RTI Elec | | UL746 | 130 °C |
| RTI Imp | | UL746 | 120 °C |
| RTI Str | | UL746 | 130 °C |
| | ASTM D648/ISO 75 | 123 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 135 ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.4 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.