PC G-3120PH TEIJIN JAPAN
PANLITE®
Engineering accessories
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| 1MHz | IEC 60250 | 3.40 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4000 Mpa | |
| bending strength | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2/5 | 65.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 4400 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 110 Mpa | |
| Flexural modulus | ISO 178 | 4400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| Tensile modulus | ASTM D638/ISO 527 | 4000 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 3.0 % |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2-0.4 % | |
| density | ASTM D792/ISO 1183 | 0.14 |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| UL flame retardant rating | 1.7mm | UL 94 | V-2 |
| 0.40mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.14 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.20-0.40 % |
| TD:4.00mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/G-3120PH |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 123 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 135 ℃（℉） | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 131 °C |
| RTI Imp | 1.7mm | UL 746 | 120 °C |
| vicat | ISO 306/B50 | 135 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 123 °C |
| RTI Elec | 1.7mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| RTI Str | 1.7mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 0.4 mm/mm.℃ |