Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 37.0 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| Shrinkage rate | | ISO294-4 | 0.10 % |
| Water absorption rate | | ISO62 | 5.3 % |
| Water absorption rate | | ISO62 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Extreme Oxygen Index 7 | | ISO4589-2 | 34 % |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VA |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA6,GFHR,12-080,GF18;ISO1043-PAGFFR(30+40+72) |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Flexural modulus | | ISO178/A | 7200 Mpa |
| Bending stress | | ISO178/A | -- Mpa |
| Bending stress | | ISO178 | 170 Mpa |
| Bending stress | | | 3.2 % |
| Tensile modulus | | ISO527-2/1 | 7960 Mpa |
| Tensile stress | | ISO527-2/5 | 110 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 50 kJ/m² |
| | ISO180/1U | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 8.6E+15 ohms |
| Volume resistivity | | IEC60093 | 5.3E+17 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 218 °C |
| | ISO75-2/A | 200 °C |
| vicat | | ISO306/B120 | 205 °C |
| Melting temperature 5 | | ISO11357-3 | 222 °C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.