Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA6 BKV20FN01 000000 LANXESS GERMANY
Durethan®
Instrument casing、Electronic and electrical、switch、Laptop case、Lighting applications、Office equipment、Connector
Heat aging
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 40 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
ISO Shortcut | ISO 1874 | PA6.GFHR.12-080.GF18;ISO1043-PAGFFR(30+40+72) |
Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
Flexural modulus | 23°C | ISO 178/A | 7200 Mpa |
bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
tensile strength | 断裂,23°C | ISO 527-2/5 | 110 Mpa |
bending strength | 23°C | ISO 178 | 170 Mpa |
Tensile modulus | 23°C | ISO 527-2/1 | 7960 Mpa |
bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 3.2 % |
Electrical performance | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
Volume resistivity | 23°C | IEC 60093 | 5.3E+17 ohms·cm |
Surface Resistivity | IEC 60093 | 8.6E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
flammability | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
0.8mm | IEC 60695-2-12 | 960 °C | |
UL flame retardant rating | 0.75mm | UL 94 | V-0 |
3.0mm | UL 94 | 5VA | |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 750 °C |
1.5mm | IEC 60695-2-13 | 750 °C | |
Limiting Oxygen Index | ISO 4589-2 | 34 % | |
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 750 °C |
physical property | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
MD:260°C,2.00mm2 | ISO 294-4 | 0.30 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.6 % |
饱和,23°C | ISO 62 | 5.3 % | |
Shrinkage rate | TD:260°C,2.00mm2 | ISO 294-4 | 0.60 % |
Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 37.0 cm3/10min |
Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV20FN01 000000 |
---|---|---|---|
melting temperature | ISO 11357-3 | 222 °C | |
vicat | ISO 306/B120 | 205 °C | |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 218 °C |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 200 °C |