ABS 10H10000
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.05 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 8.0 g/10min | |
| Shrinkage rate | 0.50 % | ||
| density | ISO 1183 | 1.05 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 8.0 g/10 min | |
| Shrinkage rate | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO 527-2/5 | 20 % | |
| Tensile modulus | ISO 527-2/5 | 2000 MPa | |
| tensile strength | ISO 527-2/5 | 38.0 MPa | |
| Tensile modulus | ISO 527-2/5 | 2000 MPa | |
| tensile strength | ISO 527-2/5 | 38.0 MPa | |
| Tensile strain | ISO 527-2/5 | 20 % | |
| Impact strength of cantilever beam gap | ISO 180/1A | 6.0 kJ/m² | |
| ISO 180/1A | 16 kJ/m² |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 6.0 kJ/m² | |
| ISO 180/1A | 16 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 650 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.