ABS 10H10000 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 10H10000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 16 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 10H10000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 20 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 38.0 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 16 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2/5 | 2000 MPa |
| Tensile strain | 断裂, 23°C | ISO 527-2/5 | 20 % |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 38.0 MPa |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| flammability | Test Condition | Test Method | 4Plas/ 10H10000 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 4Plas/ 10H10000 |
|---|---|---|---|
| density | ISO 1183 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0 kg | ISO 1133 | 8.0 g/10 min |
| Shrinkage rate | TD | 0.50 % | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | 4Plas/ 10H10000 |
|---|---|---|---|
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |