Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 44 g/10min |
| Shrinkage rate | | 内部方法 | 0.30to0.70 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| density | | ASTM D792 | 1.48 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.30to0.70 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| density | | ASTM D792 | 1.48 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | 内部方法 | 123 MPa |
| elongation | Break | 内部方法 | 10 % |
| Flexural modulus | | ASTM D790 | 8620 MPa |
| bending strength | | ASTM D790 | 167 MPa |
| tensile strength | Yield | 内部方法 | 123 MPa |
| elongation | Break | 内部方法 | 10 % |
| Flexural modulus | | ASTM D790 | 8620 MPa |
| bending strength | | ASTM D790 | 167 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+16 ohms |
| dielectric constant | | ASTM D150 | 3.30 |
| dielectric constant | | ASTM D150 | 3.30 |
| Surface Resistivity | | ASTM D257 | 1E+16 ohms |
| dielectric constant | | ASTM D150 | 3.30 |
| dielectric constant | | ASTM D150 | 3.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 255 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.8E-5到5.8E-5 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 255 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.8E-5到5.8E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.