ABS TAROBLEND 66 X0
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.20 g/cm³ | |
| melt mass-flow rate | ISO1133 | 50 g/10min | |
| Shrinkage rate | 内部方法 | 0.40到0.60 % | |
| Water absorption rate | ISO62 | 0.30 % | |
| ISO62 | 0.70 % | ||
| Shrinkage rate | 内部方法 | 0.40到0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 | |
| Burning wire flammability index | IEC60695-2-12 | 960 °C | |
| Limiting Oxygen Index | ASTMD2863 | 32 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2750 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 65.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 40 % |
| Flexural modulus | ISO178 | 2550 MPa | |
| Bending stress | ISO178 | 90.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 38 kJ/m² | |
| Impact strength of cantilever beam gap | ASTMD256 | 500 J/m | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 90.0 °C | ||
| Continuous use temperature | IEC60216 | 60.0 °C | |
| vicat | ISO306/A50 | 120 °C | |
| ISO306/B50 | 114 °C | ||
| BallPressure Test | IEC60695-10-2 | 通过 | |
| ISO11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.