Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TAROBLEND 66 X0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 66 X0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 38 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 500 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 66 X0 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2550 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 40 % |
| Tensile modulus | ISO 527-2/1 | 2750 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 MPa |
| bending strength | ISO 178 | 90.0 MPa |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 66 X0 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.7mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 32 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 66 X0 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40to0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 50 g/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.70 % |
| Shrinkage rate | TD | 内部方法 | 0.40to0.60 % |
| density | ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 66 X0 |
|---|---|---|---|
| Continuous use temperature | IEC 60216 | 60.0 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD：-30到30°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 120 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |
| vicat | -- | ISO 306/B50 | 114 °C |