Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt Index | | | 6.0 g/10min |
| Water absorption rate | | | 0.15 % |
| density | | | 1.2 g/cm |
| Resistance | Test Condition | Test Method | Test Result |
|---|
| Impact energy of cantilever beam gap | | | 907 Jm |
| Suspended hip beam without notch impact energy | | | NO BREAK |
| Electronic properties | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 2.0E+17 52-cm |
| Dielectric Strength | | | 17 KV/mm |
| Loss factor | | | 0.001 |
| optical properties | Test Condition | Test Method | Test Result |
|---|
| transmittance | | | 89 % |
| refractive index | | | 1.586 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus of elasticity | | | 2480 Mpa |
| Lazhong yield stress (yield strength) | | | 60 Mpa |
| Tensile fracture stress (fracture strength) | | | 72.4 Mpa |
| elongation at break | | | 150 % |
| flexural modulus | | | 2410 Mpa |
| heat resistance | Test Condition | Test Method | Test Result |
|---|
| Load deformation temperature (annealing) | | | 145 C |
| Load deformation temperature (unannealed) | | | |
| Vicat softening temperature point | | | 129 |
| Flammability index | Test Condition | Test Method | Test Result |
|---|
| Flame retardant grade | | | HB |
| Oxygen index | | | 26 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.